Nízkocyklová únava oceli Eurofer 97

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00313808" target="_blank" >RIV/68081723:_____/08:00313808 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Low cycle fatigue of Eurofer 97
Popis výsledku v původním jazyce
The low cycle fatigue and creep-fatigue properties of Eurofer 97 were studied. Fatigue tests have been carried out in air or in high vacuum, from room temperature to 550 °C, under total strain control. The softening behaviour as a function of the imposedstrain amplitude and temperature has been analysed in detail. At the highest test temperature, an increase of the subgrain size and carbide coarsening were observed. The microstructure of the specimens was investigated by TEM.
Název v anglickém jazyce
Low cycle fatigue of Eurofer 97
Popis výsledku anglicky
The low cycle fatigue and creep-fatigue properties of Eurofer 97 were studied. Fatigue tests have been carried out in air or in high vacuum, from room temperature to 550 °C, under total strain control. The softening behaviour as a function of the imposedstrain amplitude and temperature has been analysed in detail. At the highest test temperature, an increase of the subgrain size and carbide coarsening were observed. The microstructure of the specimens was investigated by TEM.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—

Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)