Measurement of the effective activation volume in 45XD titanium aluminides by repeated transient tests

Popis výsledku v původním jazyce

The mechanical behavior of Ti?45Al?2Mn?2Nb (at.%) containing 0.8 vol.% TiB2 was studied from room temperature up to 1090 K. The alloy shows a slight anomalous increase of flow stress with temperature around 700 K, which is rarely encountered in two-phaseg/a2 TiAl. The technique of repeated stress relaxations allows the determination of the apparent and effective activation volumes along the stress?strain curve up to 900 K. The activation volume shows two important features: (i) large variations with strain at room temperature and (ii) a sharp increase with temperature in the stress anomaly domain, indicating the existence of two different dislocation mechanisms operating, respectively, below and above the flow stress anomaly.

Název v anglickém jazyce

Measurement of the effective activation volume in 45XD titanium aluminides by repeated transient tests

Popis výsledku anglicky

The mechanical behavior of Ti?45Al?2Mn?2Nb (at.%) containing 0.8 vol.% TiB2 was studied from room temperature up to 1090 K. The alloy shows a slight anomalous increase of flow stress with temperature around 700 K, which is rarely encountered in two-phaseg/a2 TiAl. The technique of repeated stress relaxations allows the determination of the apparent and effective activation volumes along the stress?strain curve up to 900 K. The activation volume shows two important features: (i) large variations with strain at room temperature and (ii) a sharp increase with temperature in the stress anomaly domain, indicating the existence of two different dislocation mechanisms operating, respectively, below and above the flow stress anomaly.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering A-Structural materials

ISSN

0921-5093

e-ISSN

—

Svazek periodika

487

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

000257451000049

EID výsledku v databázi Scopus

—