Damage analysis of fibre-matrix system
Popis výsledku v původním jazyce
Conditions of damage initiation in fibre composite materials are analysed in the paper. The main objective of the presentation is to quantify the influence of fibre-matrix material mismatch on failure critical stress under which a crack is initiated in the vicinity of a free fibre end. The considerations are derived from the knowledge of the stress state caused by the existence of the bi-material interface. The step change of material properties in the interface leads to singular peak of stresses, whichmay be responsible for crack initiation and consequently for failure of the structure. The singular stress state near the interface is analysed by means of generalized linear elastic fracture mechanics and conditions of crack initiation are assessed. Onthe basis of the results the question of interfacial debonding between the fibre and matrix is discussed.
Název v anglickém jazyce
Damage analysis of fibre-matrix system
Popis výsledku anglicky
Conditions of damage initiation in fibre composite materials are analysed in the paper. The main objective of the presentation is to quantify the influence of fibre-matrix material mismatch on failure critical stress under which a crack is initiated in the vicinity of a free fibre end. The considerations are derived from the knowledge of the stress state caused by the existence of the bi-material interface. The step change of material properties in the interface leads to singular peak of stresses, whichmay be responsible for crack initiation and consequently for failure of the structure. The singular stress state near the interface is analysed by means of generalized linear elastic fracture mechanics and conditions of crack initiation are assessed. Onthe basis of the results the question of interfacial debonding between the fibre and matrix is discussed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA101%2F08%2F0994" target="_blank" >GA101/08/0994: Stanovení podmínek iniciace porušení v bi-materiálových vrubech složených ze dvou ortotropních materiálů</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of 17th European Conference on Fracture
ISBN
978-80-214-3692-3
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
VUTIUM Brno
Místo vydání
Brno
Místo konání akce
Brno
Datum konání akce
2. 9. 2008
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—