Kritéria iniciace trhlin ze singulárních koncentrátorů napětí. Část IV: Aplikace na povlakované konstrukce

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00322243" target="_blank" >RIV/68081723:_____/08:00322243 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crack initiation criteria for singular stress concentrations, Part IV: Applications to fracture of coated structures

Popis výsledku v původním jazyce

The influence of through crack in the protective surface layer on damage of coated structure is investigated. The coated structure is modeled as a particular case of a bi-material body consisting of thin surface layer on the substrate. Specific attentionis devoted to the case of a through coating crack with its tip at the interface between coating and the substrate. To estimate how the coating crack with its tip at the interface influences the substrate failure the general approach described in [1,2,3](Part I,II III of this contribution) is applied. An approximate approach based on calculations of crack mouth opening displacement for thin protective layers is suggested and developed. It is concluded that in the case of a stiffer coating on a more compliant substrate, the through coating cracks represent dangerous stress concentrators and, as a consequence of elastic mismatch of both materials, the critical applied stress for substrate failure decreases.

Název v anglickém jazyce

Crack initiation criteria for singular stress concentrations, Part IV: Applications to fracture of coated structures

Popis výsledku anglicky

The influence of through crack in the protective surface layer on damage of coated structure is investigated. The coated structure is modeled as a particular case of a bi-material body consisting of thin surface layer on the substrate. Specific attentionis devoted to the case of a through coating crack with its tip at the interface between coating and the substrate. To estimate how the coating crack with its tip at the interface influences the substrate failure the general approach described in [1,2,3](Part I,II III of this contribution) is applied. An approximate approach based on calculations of crack mouth opening displacement for thin protective layers is suggested and developed. It is concluded that in the case of a stiffer coating on a more compliant substrate, the through coating cracks represent dangerous stress concentrators and, as a consequence of elastic mismatch of both materials, the critical applied stress for substrate failure decreases.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Mechanics

ISSN

1802-1484

e-ISSN

—

Svazek periodika

15

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—