Interactions between TI-Al-Nb melts and Y2O3 crucibles

Popis výsledku v původním jazyce

The present paper focuses on interactions between intermetallic melts (Ti-46Al-7Nb-0.7Cr-0.1Si-0.2Ni alloy (at%)) and ceramic crucibles based on the Y2O3 refractory. Different levels of superheat and exposure time are taken into account. Vacuum inductionmelting (VIM) experiments were performed using the vacuum furnace BALZERS VSG 02. The controlled argon atmosphere inside the furnace volume was kept at the pressure level of 0.133 bar during the melting experiments. The reactions at the melt - crucibleinterface were studied by means of scanning electron microscopy (SEM) equipped with the energy dispersive x-ray analyzer (EDX). There has been clear benefit when a common refractory like alumina has been replaced by yttria. However, the results obtainedin this study show, that the long - term exposure at melting temperatures above 1650°C lead to notable reactions at the interface. We discuss the stability of the melt - ceramic system using principles of thermodynamic equilibrium.

Název v anglickém jazyce

Interactions between TI-Al-Nb melts and Y2O3 crucibles

Popis výsledku anglicky

The present paper focuses on interactions between intermetallic melts (Ti-46Al-7Nb-0.7Cr-0.1Si-0.2Ni alloy (at%)) and ceramic crucibles based on the Y2O3 refractory. Different levels of superheat and exposure time are taken into account. Vacuum inductionmelting (VIM) experiments were performed using the vacuum furnace BALZERS VSG 02. The controlled argon atmosphere inside the furnace volume was kept at the pressure level of 0.133 bar during the melting experiments. The reactions at the melt - crucibleinterface were studied by means of scanning electron microscopy (SEM) equipped with the energy dispersive x-ray analyzer (EDX). There has been clear benefit when a common refractory like alumina has been replaced by yttria. However, the results obtainedin this study show, that the long - term exposure at melting temperatures above 1650°C lead to notable reactions at the interface. We discuss the stability of the melt - ceramic system using principles of thermodynamic equilibrium.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2008. Sborník přednášek.

ISBN

978-80-254-1987-8

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

—

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí

Datum konání akce

13. 5. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—