Použití protlačovací zkoušky pro odhad vlastností tepelně ovlivněných oblastí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00325403" target="_blank" >RIV/68081723:_____/09:00325403 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Application of Small Punch Tests in Estimation of the Properties of Heat-affected Zones

Popis výsledku v původním jazyce

The small punch test technique was applied in the analysis of the creep properties of a real weld taken from a piping system used in a power plant after long-term service. The base material of the pipes was 0.5Cr-0.5Mo-0.3V steel. Specimens for small punch tests were taken from strictly localised places: from the base material, from the weld material and from the heat-affected zone. Two types of specimens for conventional creep testing were prepared from the same weld: they were cut either exclusively from the base material or as cross-weld specimens. Results of both testing types, i.e., conventional creep and small punch, are compared and discussed with the aim of demonstrating the possibility of using small punch tests to characterise the damage sensitivity of various regions of the welds.

Název v anglickém jazyce

Application of Small Punch Tests in Estimation of the Properties of Heat-affected Zones

Popis výsledku anglicky

The small punch test technique was applied in the analysis of the creep properties of a real weld taken from a piping system used in a power plant after long-term service. The base material of the pipes was 0.5Cr-0.5Mo-0.3V steel. Specimens for small punch tests were taken from strictly localised places: from the base material, from the weld material and from the heat-affected zone. Two types of specimens for conventional creep testing were prepared from the same weld: they were cut either exclusively from the base material or as cross-weld specimens. Results of both testing types, i.e., conventional creep and small punch, are compared and discussed with the aim of demonstrating the possibility of using small punch tests to characterise the damage sensitivity of various regions of the welds.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200410801" target="_blank" >IAA200410801: Numerické modelování protlačovacích zkoušek na miniaturizovaných discích z pokročilých ocelí pro spolehlivý odhad životnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Creep and Fracture in High Temperature Components - Design & Life Assessment Issues

ISBN

978-1-60595-005-1

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

DEStech Publications, Inc

Místo vydání

Lancaster, PA

Místo konání akce

Dubendorf

Datum konání akce

21. 4. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—