Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00328358" target="_blank" >RIV/68081723:_____/09:00328358 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/09:PU85297

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure

Popis výsledku v původním jazyce

Fracture toughness of nanocrystalline zirconia ceramic stabilized with 1.5 mol.% Y2O3 was measured and compared with fracture toughness of submicrometer-grained zirconia ceramics stabilized with 3 mol.% Y2O3. It was found that nanocrystalline ceramics demonstrated higher fracture toughness than submicrometer-grained zirconia ceramics with both optimized and common grain sizes. The high fracture toughness of nanocrystalline zirconia was confirmed by two different testing methods: indentation method (15.5MPa m0.5) and chevron notched beam method (7.9 MPa m0.5).

Název v anglickém jazyce

Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure

Popis výsledku anglicky

Fracture toughness of nanocrystalline zirconia ceramic stabilized with 1.5 mol.% Y2O3 was measured and compared with fracture toughness of submicrometer-grained zirconia ceramics stabilized with 3 mol.% Y2O3. It was found that nanocrystalline ceramics demonstrated higher fracture toughness than submicrometer-grained zirconia ceramics with both optimized and common grain sizes. The high fracture toughness of nanocrystalline zirconia was confirmed by two different testing methods: indentation method (15.5MPa m0.5) and chevron notched beam method (7.9 MPa m0.5).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200410502" target="_blank" >IAA200410502: Vliv nehomogenity poškození na velikostní faktor při křehkém lomu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

61

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000266225100015

EID výsledku v databázi Scopus

—