Special fracture mechanics specimens for multilayer plastic pipes testing

Popis výsledku v původním jazyce

Pipes consisting of layers of different materials (multilayer pipes) are considered. The fracture toughness value of the main pipe is taken into account as a parameter relevant to fracture assessment connected with the resistance of pipe material againstslow crack growth. With the aim of simplifying estimation of main pipe material fracture toughness, non-homogeneous test specimens cut directly from multi-layer pipes are suggested and numerically analysed. The values of the corresponding stress intensity factor KI and biaxiality factors B are calculated for the case of two and three layer test specimens. Based on the results obtained, the transferability of fracture toughness values measured on laboratory specimens to pipe systems is discussed. It isshown that in most cases of multilayer commercial pipes and routine fracture toughness measurements the values of the stress intensity factor calculated on the basis of homogeneous specimens can be used.

Název v anglickém jazyce

Special fracture mechanics specimens for multilayer plastic pipes testing

Popis výsledku anglicky

Pipes consisting of layers of different materials (multilayer pipes) are considered. The fracture toughness value of the main pipe is taken into account as a parameter relevant to fracture assessment connected with the resistance of pipe material againstslow crack growth. With the aim of simplifying estimation of main pipe material fracture toughness, non-homogeneous test specimens cut directly from multi-layer pipes are suggested and numerically analysed. The values of the corresponding stress intensity factor KI and biaxiality factors B are calculated for the case of two and three layer test specimens. Based on the results obtained, the transferability of fracture toughness values measured on laboratory specimens to pipe systems is discussed. It isshown that in most cases of multilayer commercial pipes and routine fracture toughness measurements the values of the stress intensity factor calculated on the basis of homogeneous specimens can be used.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Polymer Testing

ISSN

0142-9418

e-ISSN

—

Svazek periodika

28

Číslo periodika v rámci svazku

8

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

000271356800002

EID výsledku v databázi Scopus

—