Estimation of apparent fracture toughness of ceramic laminates
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00337562" target="_blank" >RIV/68081723:_____/09:00337562 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/09:PU81501
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Estimation of apparent fracture toughness of ceramic laminates
Popis výsledku v původním jazyce
The paper presented deals with the fracture behavior of ceramic laminates. The residual stresses in individual layers of Al2O3/5vol.%t-ZrO2 (ATZ) and Al2O3/30vol.%m-ZrO2 (AMZ) are determined. Assumptions concerning linear elastic fracture mechanics and small scale yielding are considered. In this frame the procedure based on a generalization of Sih?s strain energy density factor to the case of a crack touching the interfaces between two dissimilar materials is used for determination of effective valuesof the stress intensity factor on material interfaces. An important increase of fracture toughness at the AMZ/ATZ interface was predicted in comparison to the fracture toughness of individual material components. Predicted values were compared with dataavailable in the literature and mutual good agreement was found.
Název v anglickém jazyce
Estimation of apparent fracture toughness of ceramic laminates
Popis výsledku anglicky
The paper presented deals with the fracture behavior of ceramic laminates. The residual stresses in individual layers of Al2O3/5vol.%t-ZrO2 (ATZ) and Al2O3/30vol.%m-ZrO2 (AMZ) are determined. Assumptions concerning linear elastic fracture mechanics and small scale yielding are considered. In this frame the procedure based on a generalization of Sih?s strain energy density factor to the case of a crack touching the interfaces between two dissimilar materials is used for determination of effective valuesof the stress intensity factor on material interfaces. An important increase of fracture toughness at the AMZ/ATZ interface was predicted in comparison to the fracture toughness of individual material components. Predicted values were compared with dataavailable in the literature and mutual good agreement was found.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/KJB200410803" target="_blank" >KJB200410803: Zobecnění lineární elastické lomové mechaniky na problémy šíření trhlin v nehomogenních materiálech</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Computational Materials Science
ISSN
0927-0256
e-ISSN
—
Svazek periodika
46
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
000270346300013
EID výsledku v databázi Scopus
—