Short crack growth in polycrystalline materials

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00352811" target="_blank" >RIV/68081723:_____/10:00352811 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Short crack growth in polycrystalline materials

Popis výsledku v původním jazyce

The early stages of fatigue damage in cyclic loading in several polycrystalline materials were studied. The initiation of fatigue cracks is influenced by a number of factors like the presence of inclusions, grain size and cyclic creep strain. The growthof short cracks was measured in symmetrical loading and in cycling with positive mean stress. The kinetics of short crack growth is affected by the presence of secondary cracks and can be approximated by an exponential law. The integrated crack growth law is equivalent to Coffin-Manson law allowing the interpretation of this law in terms of short crack growth.

Název v anglickém jazyce

Short crack growth in polycrystalline materials

Popis výsledku anglicky

The early stages of fatigue damage in cyclic loading in several polycrystalline materials were studied. The initiation of fatigue cracks is influenced by a number of factors like the presence of inclusions, grain size and cyclic creep strain. The growthof short cracks was measured in symmetrical loading and in cycling with positive mean stress. The kinetics of short crack growth is affected by the presence of secondary cracks and can be approximated by an exponential law. The integrated crack growth law is equivalent to Coffin-Manson law allowing the interpretation of this law in terms of short crack growth.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F07%2F1500" target="_blank" >GA101/07/1500: Nové principy pro predikci životnosti strojních součástí zatěžovaných proměnnými silami</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Procedia Engineering

ISSN

1877-7058

e-ISSN

—

Svazek periodika

2

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

10

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—