Microstructure and impact response of high-chromium ODS steels
Popis výsledku v původním jazyce
A new class of ODS steels alloyed by Cr and W is developed as a high temperature structural material for prospective power sources, the fission reactors of IV generation and the fusion reactors. The aim of the work was to investigate the influence of microstructure on the fracture properties of ODS (9-18)Cr-W-Ti-Y2O3 steels. It was found that the increasing in the Cr and W content brought to the steels strength at elevated temperatures and increased upper shelf energy level and shifted transition regiontowards lower temperatures. The increase in the yttria content led to the decreasing the upper shelf energy and shifted the TDBTT towards higher temperatures. The impact energy of rolled ODS sheet depended strongly on the fracture plane orientation regarding to the rolling direction. The splitting edges profile changed according to the sample orientation and thus the energy portion consumed for the shearing was changed.
Název v anglickém jazyce
Microstructure and impact response of high-chromium ODS steels
Popis výsledku anglicky
A new class of ODS steels alloyed by Cr and W is developed as a high temperature structural material for prospective power sources, the fission reactors of IV generation and the fusion reactors. The aim of the work was to investigate the influence of microstructure on the fracture properties of ODS (9-18)Cr-W-Ti-Y2O3 steels. It was found that the increasing in the Cr and W content brought to the steels strength at elevated temperatures and increased upper shelf energy level and shifted transition regiontowards lower temperatures. The increase in the yttria content led to the decreasing the upper shelf energy and shifted the TDBTT towards higher temperatures. The impact energy of rolled ODS sheet depended strongly on the fracture plane orientation regarding to the rolling direction. The splitting edges profile changed according to the sample orientation and thus the energy portion consumed for the shearing was changed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F08%2F1397" target="_blank" >GA106/08/1397: Vliv ultrajemné disperze částic na štěpný lom chromových ocelí</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
New Methods of Damage and Failure Analysis of Structural Parts
ISBN
978-80-248-2265-5
ISSN
—
e-ISSN
—
Počet stran výsledku
7
Strana od-do
—
Název nakladatele
VŠB - TU Ostrava
Místo vydání
Ostrava
Místo konání akce
Ostrava
Datum konání akce
6. 9. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—