Numerical determination of the crack front shape for a specimen with finite thickness

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00353464" target="_blank" >RIV/68081723:_____/10:00353464 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Numerical determination of the crack front shape for a specimen with finite thickness

Popis výsledku v původním jazyce

The iterative process for estimation of a real crack front based on a stress singularity exponent is presented. The crack front was approximated by a spline curve. In each node defining the crack front the stress singularity exponent has been estimated and complete crack front shape was found. The difference between thin and thick specimens is described and discussed. The methodology presented can help to estimate crack front shape in a linear elastic fracture mechanics framework and estimate fracture parameters of cracks more accurately. Therefore, the results presented can be helpful for a better understanding of fatigue failure and more reliable prediction of their residual lifetime.

Název v anglickém jazyce

Numerical determination of the crack front shape for a specimen with finite thickness

Popis výsledku anglicky

The iterative process for estimation of a real crack front based on a stress singularity exponent is presented. The crack front was approximated by a spline curve. In each node defining the crack front the stress singularity exponent has been estimated and complete crack front shape was found. The difference between thin and thick specimens is described and discussed. The methodology presented can help to estimate crack front shape in a linear elastic fracture mechanics framework and estimate fracture parameters of cracks more accurately. Therefore, the results presented can be helpful for a better understanding of fatigue failure and more reliable prediction of their residual lifetime.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

XV International Colloquim Mechanical Fatigue of Metals

ISBN

978-83-60691-83-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Opole University of Technology

Místo vydání

Opole

Místo konání akce

Opole

Datum konání akce

13. 9. 2010

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—