The effect of a free surface on fatigue crack behaviour
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354030" target="_blank" >RIV/68081723:_____/10:00354030 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/10:PU87726
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The effect of a free surface on fatigue crack behaviour
Popis výsledku v původním jazyce
The effect of a free surface on fatigue crack behaviour is discussed in the paper and generalized stress intensity factor methodology is used for a reliable estimation of the fatigue crack propagation rate in the area close to a free surface, where the effect of vertex singularity is important. It is shown that a decrease in the stress singularity exponent close to the vertex point leads to a decrease in the fatigue crack propagation rate and contributes to a typical curved crack front shape. The numerical estimations of the crack shape correspond well with experimental observations taken from the literature. The proposed methodology facilitates explanation of the experimentally observed decrease in the fatigue crack propagation rate (FCPR) for thin structures. It is shown, that decrease of FCPR depends on Poisson?s ratio and parameters of the Paris?Erdogan law for corresponding materials.
Název v anglickém jazyce
The effect of a free surface on fatigue crack behaviour
Popis výsledku anglicky
The effect of a free surface on fatigue crack behaviour is discussed in the paper and generalized stress intensity factor methodology is used for a reliable estimation of the fatigue crack propagation rate in the area close to a free surface, where the effect of vertex singularity is important. It is shown that a decrease in the stress singularity exponent close to the vertex point leads to a decrease in the fatigue crack propagation rate and contributes to a typical curved crack front shape. The numerical estimations of the crack shape correspond well with experimental observations taken from the literature. The proposed methodology facilitates explanation of the experimentally observed decrease in the fatigue crack propagation rate (FCPR) for thin structures. It is shown, that decrease of FCPR depends on Poisson?s ratio and parameters of the Paris?Erdogan law for corresponding materials.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
International Journal of Fatigue
ISSN
0142-1123
e-ISSN
—
Svazek periodika
32
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000278281100005
EID výsledku v databázi Scopus
—