Fatigue crack propagation in thin structures

Popis výsledku v původním jazyce

The influence of specimen thickness on fatigue crack behaviour has been investigated. To this aim the fatigue crack propagation rate has been measured on two different types of test specimens with varying thickness. The change of stress singularity exponent for the crack front due to vicinity of the free surface is considered. To explain the effect of stress singularity changes on obtained experimental results a methodology based on generalized stress intensity factor and strain energy density concept has been used. It is shown that for materials with Poisson?s ratio of about 0.3 the free surface effect does not play a decisive role for specimens with a low level of in-plane constraint but can influence fatigue crack propagation rate in the case of geometries with a high level of the constraint.

Název v anglickém jazyce

Fatigue crack propagation in thin structures

Popis výsledku anglicky

The influence of specimen thickness on fatigue crack behaviour has been investigated. To this aim the fatigue crack propagation rate has been measured on two different types of test specimens with varying thickness. The change of stress singularity exponent for the crack front due to vicinity of the free surface is considered. To explain the effect of stress singularity changes on obtained experimental results a methodology based on generalized stress intensity factor and strain energy density concept has been used. It is shown that for materials with Poisson?s ratio of about 0.3 the free surface effect does not play a decisive role for specimens with a low level of in-plane constraint but can influence fatigue crack propagation rate in the case of geometries with a high level of the constraint.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

417-418

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000279319200065

EID výsledku v databázi Scopus

—