Crack Behaviour in Laminar Ceramics with Strong Interfaces
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354085" target="_blank" >RIV/68081723:_____/10:00354085 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/09:PU82521
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crack Behaviour in Laminar Ceramics with Strong Interfaces
Popis výsledku v původním jazyce
The paper deals with crack propagation in ceramic laminates. Assumptions of linear elastic fracture mechanics and small scale yielding are considered. Crack behaviour in a ceramic laminate body under external loading is investigated. Strong residual stresses due to different coefficients of thermal expansion of individual material layers are taken into account in finite element calculations. The change of crack propagation direction at the material interface is estimated on the base of the strain energydensity factor and maximum tangential stress criteria. The influence of thickness of laminate layers on crack propagation direction is estimated. The stepwise crack propagation through the Al2O3-ZrO2 ceramic laminate is numerically estimated. It can beconcluded that good agreement between the estimated crack path and experimental data was found.
Název v anglickém jazyce
Crack Behaviour in Laminar Ceramics with Strong Interfaces
Popis výsledku anglicky
The paper deals with crack propagation in ceramic laminates. Assumptions of linear elastic fracture mechanics and small scale yielding are considered. Crack behaviour in a ceramic laminate body under external loading is investigated. Strong residual stresses due to different coefficients of thermal expansion of individual material layers are taken into account in finite element calculations. The change of crack propagation direction at the material interface is estimated on the base of the strain energydensity factor and maximum tangential stress criteria. The influence of thickness of laminate layers on crack propagation direction is estimated. The stepwise crack propagation through the Al2O3-ZrO2 ceramic laminate is numerically estimated. It can beconcluded that good agreement between the estimated crack path and experimental data was found.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials
ISSN
1013-9826
e-ISSN
—
Svazek periodika
417-418
Číslo periodika v rámci svazku
-
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000279319200076
EID výsledku v databázi Scopus
—