Accelerated test for PE 100 and PE 100 RC pipes grades

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354137" target="_blank" >RIV/68081723:_____/10:00354137 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Accelerated test for PE 100 and PE 100 RC pipes grades

Popis výsledku v původním jazyce

The failure mode called long time brittle failure (due to small crack growth ? SCG) limits the lifetime of plastic pipes. Nowadays there are two accelerated tests (PENT and FNCT) that enable to estimate the lifetime of HDPE using in plastics pipes. For unimodal grade the time to failure according these accelerated tests is about tens hours, for bimodal grade PE 100 it is roughly thousands hours and for the new PE 100 RC grade is greater than 1 year. For the HDPE pipes grade with higher resistance against SCG some modification or alternatively new tests should be developed that enable even for these materials to obtain the results in relatively short time. In this contribution we focused mainly on some modification of PENT and FNCT and possible correlation between mechanical and structural test.

Název v anglickém jazyce

Accelerated test for PE 100 and PE 100 RC pipes grades

Popis výsledku anglicky

The failure mode called long time brittle failure (due to small crack growth ? SCG) limits the lifetime of plastic pipes. Nowadays there are two accelerated tests (PENT and FNCT) that enable to estimate the lifetime of HDPE using in plastics pipes. For unimodal grade the time to failure according these accelerated tests is about tens hours, for bimodal grade PE 100 it is roughly thousands hours and for the new PE 100 RC grade is greater than 1 year. For the HDPE pipes grade with higher resistance against SCG some modification or alternatively new tests should be developed that enable even for these materials to obtain the results in relatively short time. In this contribution we focused mainly on some modification of PENT and FNCT and possible correlation between mechanical and structural test.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Polymeric Materials Halle/Saale

ISBN

978-3-86829-282-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Martin Luther University

Místo vydání

Halle-Wittenberg

Místo konání akce

Halle/Saale

Datum konání akce

15. 9. 2010

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—