High temperature service embrittlement of EUROFER´97 steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354284" target="_blank" >RIV/68081723:_____/10:00354284 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/10:PU89160
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
High temperature service embrittlement of EUROFER´97 steel
Popis výsledku v původním jazyce
The aim of the work was to describe effect of long-time ageing on the microstructure and fracture properties of the Eurofer´97 steel. The embrittlement of the high chromium ferritic-martensitic implies important limitation for use of these steels causingcarbide coarsening and/or intercrystalline embrittlement. Detailed microstructure studies were carried out on the steel in as-received state and in state after long-time thermal ageing for 550°C/5.000 h. Mechanical properties were evaluated by means ofCharpy impact testing. Only a slight growth of the particles and partial recrystalization of the subgrains after thermal ageing has been observed. The isothermal ageing caused shift in tDBTT about +5°C Degradation of the impact properties was probably caused by synergic effect of carbide coarsening and mind recrystalization of the subgrains
Název v anglickém jazyce
High temperature service embrittlement of EUROFER´97 steel
Popis výsledku anglicky
The aim of the work was to describe effect of long-time ageing on the microstructure and fracture properties of the Eurofer´97 steel. The embrittlement of the high chromium ferritic-martensitic implies important limitation for use of these steels causingcarbide coarsening and/or intercrystalline embrittlement. Detailed microstructure studies were carried out on the steel in as-received state and in state after long-time thermal ageing for 550°C/5.000 h. Mechanical properties were evaluated by means ofCharpy impact testing. Only a slight growth of the particles and partial recrystalization of the subgrains after thermal ageing has been observed. The isothermal ageing caused shift in tDBTT about +5°C Degradation of the impact properties was probably caused by synergic effect of carbide coarsening and mind recrystalization of the subgrains
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Metallurgica Slovaca
ISSN
1335-1532
e-ISSN
—
Svazek periodika
1
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—