Nanopowders with superparamagnetic Fe3C particles and their annealing behaviour
Popis výsledku v původním jazyce
Two samples of nanopowders containing superparamagnetic Fe3C and Fe3O4/gamma-Fe2O3 particles and carbon black were synthesized by the method of laser-induced homogeneous pyrolysis of gaseous precursors. Both were characterized by XRD, HR-TEM, Mössbauer spectrometry and standard magnetic measurements. The mean crystallite size of Fe3C was 3 nm for the first sample and 10 nm for the second sample. Fe3C phase in both samples exhibited reduced Curie temperature and smeared ferromagnetic-paramagnetic transition. After annealing of the samples at 800°C for 30min the Curie temperature of the recrystallized Fe3C phase in both samples was 214°C (standard bulk value).
Název v anglickém jazyce
Nanopowders with superparamagnetic Fe3C particles and their annealing behaviour
Popis výsledku anglicky
Two samples of nanopowders containing superparamagnetic Fe3C and Fe3O4/gamma-Fe2O3 particles and carbon black were synthesized by the method of laser-induced homogeneous pyrolysis of gaseous precursors. Both were characterized by XRD, HR-TEM, Mössbauer spectrometry and standard magnetic measurements. The mean crystallite size of Fe3C was 3 nm for the first sample and 10 nm for the second sample. Fe3C phase in both samples exhibited reduced Curie temperature and smeared ferromagnetic-paramagnetic transition. After annealing of the samples at 800°C for 30min the Curie temperature of the recrystallized Fe3C phase in both samples was 214°C (standard bulk value).
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Surface and Interface Analysis
ISSN
0142-2421
e-ISSN
—
Svazek periodika
42
Číslo periodika v rámci svazku
6-7
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000281149700054
EID výsledku v databázi Scopus
—