Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 °C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354549" target="_blank" >RIV/68081723:_____/10:00354549 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 °C

Popis výsledku v původním jazyce

Fatigue crack initiation and propagation was studied in cast polycrystalline nickel base superalloy Inconel 713LC in as-received condition and with surface treatment by AlSi protective coating. Cylindrical specimens were cyclically strained under straincontrol with constant total strain amplitude at 800 C. Fatigue fracture surface, specimen surface, and specimen sections were investigated using optical microscopy and scanning electron microscopy. Fatigue crack initiation sites and fatigue crack growthmechanisms were identified and crack propagation rates were obtained base on striation spacing in fracture surfaces. The crack initiation mechanism study revealed reasons for the fatigue life increase in the surface treated material.

Název v anglickém jazyce

Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 °C

Popis výsledku anglicky

Fatigue crack initiation and propagation was studied in cast polycrystalline nickel base superalloy Inconel 713LC in as-received condition and with surface treatment by AlSi protective coating. Cylindrical specimens were cyclically strained under straincontrol with constant total strain amplitude at 800 C. Fatigue fracture surface, specimen surface, and specimen sections were investigated using optical microscopy and scanning electron microscopy. Fatigue crack initiation sites and fatigue crack growthmechanisms were identified and crack propagation rates were obtained base on striation spacing in fracture surfaces. The crack initiation mechanism study revealed reasons for the fatigue life increase in the surface treated material.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Sborník vědeckých prací Vysoké školy báňské - Technické univerzity Ostrava

ISSN

1210-0471

e-ISSN

—

Svazek periodika

56

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—