Reliability assessment of an interface related singular stress concentrations
Popis výsledku v původním jazyce
In the paper the fracture mechanics properties of the bi-material notches are assessed by generalizing the standard crack linear elastic fracture mechanics for homogeneous media. First the singular stress field near the bi-material notch tip is investigated. Then criteria for the crack initiation and its subsequent propagation direction are formulated. To this aim it is supposed that the mechanism of crack propagation from the bi-material notch and that in the case of a crack in homogeneous materials isthe same. In the contribution the stress and the energy approaches are used to assess the fracture initiation. In the case of the stress concentrations connected with material interface, more than one failure manner are possible. The damage manner caused by the existence of the bi-material notch will be evaluated and discussed.
Název v anglickém jazyce
Reliability assessment of an interface related singular stress concentrations
Popis výsledku anglicky
In the paper the fracture mechanics properties of the bi-material notches are assessed by generalizing the standard crack linear elastic fracture mechanics for homogeneous media. First the singular stress field near the bi-material notch tip is investigated. Then criteria for the crack initiation and its subsequent propagation direction are formulated. To this aim it is supposed that the mechanism of crack propagation from the bi-material notch and that in the case of a crack in homogeneous materials isthe same. In the contribution the stress and the energy approaches are used to assess the fracture initiation. In the case of the stress concentrations connected with material interface, more than one failure manner are possible. The damage manner caused by the existence of the bi-material notch will be evaluated and discussed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Multiscaling of Synthetic and Natural Systems with Self-Adaptive Capability
ISBN
978-986-02-3909-6
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
—
Název nakladatele
National Taiwan University of Science and Technology
Místo vydání
Taipei
Místo konání akce
Taipei
Datum konání akce
21. 6. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—