A study of phase transformations in complex matallic alloys Al73Mn23Pd4 and Al73Mn21Pd6

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00352180" target="_blank" >RIV/68081723:_____/11:00352180 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A study of phase transformations in complex matallic alloys Al73Mn23Pd4 and Al73Mn21Pd6

Popis výsledku v původním jazyce

The microstructure characterization of Al73Mn23Pd4 and Al73Mn21Pd6 alloys was done after annealing at 900oC for 312 h and subsequent water quenching, as well as after thermat cycling. DTA and EDX/WDX/SEM techniques were used in the investigation. It wasfound out that the alloys consist of the single ternary T-phase after annealing and water quenching. The DTA experiment confirmed the stability of this phase also at lower temperatures. After DTA, the alloys exhibited double-phase microstructure consisting of the ternary T-phase and probably the icosahedral I-phase. It was proved an incongruent transformation of the ternary T-phase into the liquid and vice versa.

Název v anglickém jazyce

A study of phase transformations in complex matallic alloys Al73Mn23Pd4 and Al73Mn21Pd6

Popis výsledku anglicky

The microstructure characterization of Al73Mn23Pd4 and Al73Mn21Pd6 alloys was done after annealing at 900oC for 312 h and subsequent water quenching, as well as after thermat cycling. DTA and EDX/WDX/SEM techniques were used in the investigation. It wasfound out that the alloys consist of the single ternary T-phase after annealing and water quenching. The DTA experiment confirmed the stability of this phase also at lower temperatures. After DTA, the alloys exhibited double-phase microstructure consisting of the ternary T-phase and probably the icosahedral I-phase. It was proved an incongruent transformation of the ternary T-phase into the liquid and vice versa.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

465

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—