Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00354599" target="_blank" >RIV/68081723:_____/11:00354599 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Arcan-Richard Specimens: Is There a Pure Shear Mode?

Popis výsledku v původním jazyce

Traditionally, applications of fracture mechanics have been mainly focused on cracks growing under the opening or mode I mechanism (three point bend specimen, middle tension specimen, crack tension specimen, etc.). When investigating instability under mixed mode loading conditions, three different alternatives can be envisaged consisting of: a) machining a hole in standard specimens, b) creating a crack oriented under a given angle, and c) using non-standard Arcan-Richard specimens. In this work, finiteelement calculations are performed to analyze the initial values of the fracture parameters in Arcan-Richard specimens. First, the influence of the normal stress mode to the shear stress mode ratio is analyzed, then the effect of the constraint level isdiscussed, and finally, the initial propagation angle of the daughter crack is derived.

Název v anglickém jazyce

Arcan-Richard Specimens: Is There a Pure Shear Mode?

Popis výsledku anglicky

Traditionally, applications of fracture mechanics have been mainly focused on cracks growing under the opening or mode I mechanism (three point bend specimen, middle tension specimen, crack tension specimen, etc.). When investigating instability under mixed mode loading conditions, three different alternatives can be envisaged consisting of: a) machining a hole in standard specimens, b) creating a crack oriented under a given angle, and c) using non-standard Arcan-Richard specimens. In this work, finiteelement calculations are performed to analyze the initial values of the fracture parameters in Arcan-Richard specimens. First, the influence of the normal stress mode to the shear stress mode ratio is analyzed, then the effect of the constraint level isdiscussed, and finally, the initial propagation angle of the daughter crack is derived.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F09%2F0867" target="_blank" >GA101/09/0867: Odhad únavového poškození tenkostěnných struktur</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

452-453

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—