Fatigue property and fatigue cracks of ultra-fine grained copper processed by equal-channel angular pressing
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00358391" target="_blank" >RIV/68081723:_____/11:00358391 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue property and fatigue cracks of ultra-fine grained copper processed by equal-channel angular pressing
Popis výsledku v původním jazyce
Fatigue life, cyclic deformation behavior and microstructure of ultrafine-grained (UFG) copper produced by ECAP were tested and observed. Development of surface relief and fracture surfaces was observed. The results show that the UFG Cu has lower ductility and its strain controlled cyclic properties are worse than those of lower strength conventional grained counterparts. All the ECAP specimens display obvious cyclic softening under the applied range. The cyclic softening ratio increases with increasingstrain amplitude. The formation of shear bands and grain boundary sliding are the main factors causing fatigue crack nucleation as well as the fatigue failure.
Název v anglickém jazyce
Fatigue property and fatigue cracks of ultra-fine grained copper processed by equal-channel angular pressing
Popis výsledku anglicky
Fatigue life, cyclic deformation behavior and microstructure of ultrafine-grained (UFG) copper produced by ECAP were tested and observed. Development of surface relief and fracture surfaces was observed. The results show that the UFG Cu has lower ductility and its strain controlled cyclic properties are worse than those of lower strength conventional grained counterparts. All the ECAP specimens display obvious cyclic softening under the applied range. The cyclic softening ratio increases with increasingstrain amplitude. The formation of shear bands and grain boundary sliding are the main factors causing fatigue crack nucleation as well as the fatigue failure.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials
ISSN
1013-9826
e-ISSN
—
Svazek periodika
2011
Číslo periodika v rámci svazku
682
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
7
Strana od-do
231-237
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—