Fatigue crack propagation within the austempered ductile iron microstructure
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00366908" target="_blank" >RIV/68081723:_____/11:00366908 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue crack propagation within the austempered ductile iron microstructure
Popis výsledku v původním jazyce
Austempered ductile iron (ADI) is a material with a wide range of potential application, especially in the automotive and earth moving machinery industries. Cast components usually subjected to variable dynamic loading may fail by sudden, unexpected fatigue fractures. Thus, fatigue crack propagation resistance is one of the most important material properties. The aim of this contribution is to determine the fatigue crack propagation curve da/dN vs. Ka and the threshold amplitude of stress intensity factor Kath. Microstructure and its influence on crack initiation and propagation is analyzed. A diversity of crack propagation modes at low Ka and high Ka was observed.
Název v anglickém jazyce
Fatigue crack propagation within the austempered ductile iron microstructure
Popis výsledku anglicky
Austempered ductile iron (ADI) is a material with a wide range of potential application, especially in the automotive and earth moving machinery industries. Cast components usually subjected to variable dynamic loading may fail by sudden, unexpected fatigue fractures. Thus, fatigue crack propagation resistance is one of the most important material properties. The aim of this contribution is to determine the fatigue crack propagation curve da/dN vs. Ka and the threshold amplitude of stress intensity factor Kath. Microstructure and its influence on crack initiation and propagation is analyzed. A diversity of crack propagation modes at low Ka and high Ka was observed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Metallurgica Slovaca
ISSN
1338-1156
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
8
Strana od-do
18-25
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—