Cyclic plasticity and cyclic creep in austenitic-ferritic duplex steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00370009" target="_blank" >RIV/68081723:_____/11:00370009 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Cyclic plasticity and cyclic creep in austenitic-ferritic duplex steel

Popis výsledku v původním jazyce

Smooth specimens made from austenitic-ferritic duplex steel were subjected to constant stress amplitude loading with positive mean stresses. Hysteresis loops were recorded during the fatigue life and plastic strain amplitude and cyclic creep rate were determined. Fatigue hardening/softening curves, cyclic creep curves and cyclic stress-strain curves for different positive mean stresses were evaluated. Typical dislocation structures developed in both phases of the duplex steel were identified using TEM,compared with the saturated plastic strain amplitude and correlated with the decrease of the cyclic creep rate during cycling and the slope of the cyclic stress-strain curve.

Název v anglickém jazyce

Cyclic plasticity and cyclic creep in austenitic-ferritic duplex steel

Popis výsledku anglicky

Smooth specimens made from austenitic-ferritic duplex steel were subjected to constant stress amplitude loading with positive mean stresses. Hysteresis loops were recorded during the fatigue life and plastic strain amplitude and cyclic creep rate were determined. Fatigue hardening/softening curves, cyclic creep curves and cyclic stress-strain curves for different positive mean stresses were evaluated. Typical dislocation structures developed in both phases of the duplex steel were identified using TEM,compared with the saturated plastic strain amplitude and correlated with the decrease of the cyclic creep rate during cycling and the slope of the cyclic stress-strain curve.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F07%2F1500" target="_blank" >GA101/07/1500: Nové principy pro predikci životnosti strojních součástí zatěžovaných proměnnými silami</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

465

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

431-434

Kód UT WoS článku

000291704700100

EID výsledku v databázi Scopus

—