The influence of discontinuity of fracture-mechanics parameters on the failure manner of multi-material structures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00370064" target="_blank" >RIV/68081723:_____/11:00370064 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The influence of discontinuity of fracture-mechanics parameters on the failure manner of multi-material structures

Popis výsledku v původním jazyce

Within failure assessment of singular stress concentrators, the crack initiation and propagation direction is often gained from the criterion of the maximum tangential stress. But there are cases where the crack is initiated in a different direction thanthe direction corresponding to the global maximum of tangential stress. A case of this kind can occur during constrained crack initiation caused by discontinuity of fracture-mechanics parameters, namely the fracture toughness KIC or the threshold valueKIth. An example can be the crack initiation in a multi-material wedge, where the extreme value of tangential stress occurs in one of the materials, but the crack initiates in another material part. The maximum value of tangential stress is often oriented to the material with the highest elastic module. But due to different fracture-mechanics properties (KIC or KIth) of particular materials, the crack can initiate into a material with worse fracture-mechanics properties or into the bi-ma

Název v anglickém jazyce

The influence of discontinuity of fracture-mechanics parameters on the failure manner of multi-material structures

Popis výsledku anglicky

Within failure assessment of singular stress concentrators, the crack initiation and propagation direction is often gained from the criterion of the maximum tangential stress. But there are cases where the crack is initiated in a different direction thanthe direction corresponding to the global maximum of tangential stress. A case of this kind can occur during constrained crack initiation caused by discontinuity of fracture-mechanics parameters, namely the fracture toughness KIC or the threshold valueKIth. An example can be the crack initiation in a multi-material wedge, where the extreme value of tangential stress occurs in one of the materials, but the crack initiates in another material part. The maximum value of tangential stress is often oriented to the material with the highest elastic module. But due to different fracture-mechanics properties (KIC or KIth) of particular materials, the crack can initiate into a material with worse fracture-mechanics properties or into the bi-ma

Druh

O - Ostatní výsledky

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F2049" target="_blank" >GAP108/10/2049: Iniciace a šíření trhliny ze singulárních koncentrátorů napětí souvisejících s rozhraním</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů