Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 °C

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00370071" target="_blank" >RIV/68081723:_____/11:00370071 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 °C
Popis výsledku v původním jazyce
This paper is focused on the study of initiation and growth of fatigue cracks in IN713LC with Al protective coating and without coating. Microstructure characteristics and microhardness of Al coating are documented. Fatigue crack initiation and fatigue crack growth mechanisms were identified. The crack propagation rates were obtained based on striation spacing in fracture surfaces.
Název v anglickém jazyce
Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 °C
Popis výsledku anglicky
This paper is focused on the study of initiation and growth of fatigue cracks in IN713LC with Al protective coating and without coating. Microstructure characteristics and microhardness of Al coating are documented. Fatigue crack initiation and fatigue crack growth mechanisms were identified. The crack propagation rates were obtained based on striation spacing in fracture surfaces.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—

Projekt
<a href="/cs/project/GAP107%2F11%2F2065" target="_blank" >GAP107/11/2065: Ochranné difúzní povrchové vrstvy pro vysokoteplotní aplikaci u litých niklových superslitin</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)