Compressive Creep Tests of An Aluminium Powder Composite Reinforced by Ceramic Particles

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00375109" target="_blank" >RIV/68081723:_____/11:00375109 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Compressive Creep Tests of An Aluminium Powder Composite Reinforced by Ceramic Particles

Popis výsledku v původním jazyce

The aim of this work is to study of a composite mixture of aluminium powders, to analyze of composite microstructure and mostly to describe the creep behaviour of composite in compression. The experimental material was based on Al powder matrix (Al 99%)about the particle size of less than 200 ?m. This powder was mixtured with silicon carbide particles (SiC) having the size about 10 ?m. The Al composite powder was prepared via conventional direct hot-extrusion (DE) at temperature 450°C. The microstructural investigations were performed using OM and SEM. It was found that DE process exhibits some breaking of carbide particles to size of range from 0.5 to 5 ?m. Creep tests in compression were conducted at temperatures 423 -623 K and at applied stresses in the range from 60 to 100 MPa. Consequently, for an evaluation of controlling creep mechanisms an activation energy of creep and the stress exponent of the creep rate were determined.

Název v anglickém jazyce

Compressive Creep Tests of An Aluminium Powder Composite Reinforced by Ceramic Particles

Popis výsledku anglicky

The aim of this work is to study of a composite mixture of aluminium powders, to analyze of composite microstructure and mostly to describe the creep behaviour of composite in compression. The experimental material was based on Al powder matrix (Al 99%)about the particle size of less than 200 ?m. This powder was mixtured with silicon carbide particles (SiC) having the size about 10 ?m. The Al composite powder was prepared via conventional direct hot-extrusion (DE) at temperature 450°C. The microstructural investigations were performed using OM and SEM. It was found that DE process exhibits some breaking of carbide particles to size of range from 0.5 to 5 ?m. Creep tests in compression were conducted at temperatures 423 -623 K and at applied stresses in the range from 60 to 100 MPa. Consequently, for an evaluation of controlling creep mechanisms an activation energy of creep and the stress exponent of the creep rate were determined.

Druh

D - Stať ve sborníku

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/KJB200410801" target="_blank" >KJB200410801: Studium nano-strukturních materiálů konsolidovaných z práškových kompaktů technikou ECAP</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metal 2011

ISBN

978-80-87294-24-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

"Paper no. 977"

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

18. 5. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—