Analysis of the effective and internal cyclic stress components in cast gama?TiAl based alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00435368" target="_blank" >RIV/68081723:_____/11:00435368 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of the effective and internal cyclic stress components in cast gama?TiAl based alloy

Popis výsledku v původním jazyce

Cyclic strain controlled multiple step tests in air have been performed on cylindrical specimens of cast gama-based alloy Ti?48Al?2Nb?2Cr?0.82B at. % with nearly lamellar microstructure of gamaandalpha2 phases at 23 and 750 °C. The objective was to analyze the internal and effective cyclic stress components which were derived from the hysteresis loops analyzed according to the statistical theory of hysteresis loop. Dislocation structures in cyclically strained specimens at room temperature were observedusing TEM. Cyclic response at both temperatures was compared and discussed in relation to changes of internal and effective stress components and dislocation modes in gamaphase observed and referred in the literature.

Název v anglickém jazyce

Analysis of the effective and internal cyclic stress components in cast gama?TiAl based alloy

Popis výsledku anglicky

Cyclic strain controlled multiple step tests in air have been performed on cylindrical specimens of cast gama-based alloy Ti?48Al?2Nb?2Cr?0.82B at. % with nearly lamellar microstructure of gamaandalpha2 phases at 23 and 750 °C. The objective was to analyze the internal and effective cyclic stress components which were derived from the hysteresis loops analyzed according to the statistical theory of hysteresis loop. Dislocation structures in cyclically strained specimens at room temperature were observedusing TEM. Cyclic response at both temperatures was compared and discussed in relation to changes of internal and effective stress components and dislocation modes in gamaphase observed and referred in the literature.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F11%2F0704" target="_blank" >GAP107/11/0704: Optimalizace struktury a vlastnosti moderních vysokoteplotních litých materiálů legovaných uhlíkem pomocí komplexního tepelného zpracování</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

3rd International Conference on Heterogeneous Material Mechanics (ICHMM 2011)

ISBN

978-1-60595-054-9

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

921-924

Název nakladatele

Destech Publications

Místo vydání

Lancaster

Místo konání akce

Shanghai

Datum konání akce

22. 5. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000297713100223