Hydrogen Storage Capacity of Mg/Mg2Ni Eutectic Doped with Elements from Groups XIII and XIV

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00377933" target="_blank" >RIV/68081723:_____/12:00377933 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hydrogen Storage Capacity of Mg/Mg2Ni Eutectic Doped with Elements from Groups XIII and XIV

Popis výsledku v původním jazyce

In the present paper, the chemical composition of Mg-8.5 at.% Ni-2.7at.%X alloys (X ? elements of the 13th and 14th groups) as prospective hydrogen storage was investigated. Experimental alloys were studied in three states: (i) after stabilization anneal, (ii) after stabilization anneal and hydrogen charging, and (iii) after stabilization anneal, hydrogen charging and hydrogen desorption. It was ascertained that a ratio of concentration of X in two principal phases ? Mg2NiH4(-X) and MgH2(-X) ? was a decreasing function of the ionization potential of X. The stronger the preference of X for Mg2NiH4-X phase, the higher the hydrogen storage capacity of Mg-Ni-X alloy was. For X = In, the hydrogen storage capacity was slightly higher than the capacity of anun-alloyed binary eutectic Mg-Ni alloy.

Název v anglickém jazyce

Hydrogen Storage Capacity of Mg/Mg2Ni Eutectic Doped with Elements from Groups XIII and XIV

Popis výsledku anglicky

In the present paper, the chemical composition of Mg-8.5 at.% Ni-2.7at.%X alloys (X ? elements of the 13th and 14th groups) as prospective hydrogen storage was investigated. Experimental alloys were studied in three states: (i) after stabilization anneal, (ii) after stabilization anneal and hydrogen charging, and (iii) after stabilization anneal, hydrogen charging and hydrogen desorption. It was ascertained that a ratio of concentration of X in two principal phases ? Mg2NiH4(-X) and MgH2(-X) ? was a decreasing function of the ionization potential of X. The stronger the preference of X for Mg2NiH4-X phase, the higher the hydrogen storage capacity of Mg-Ni-X alloy was. For X = In, the hydrogen storage capacity was slightly higher than the capacity of anun-alloyed binary eutectic Mg-Ni alloy.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2012 Conference Proceedings

ISBN

978-80-87294-31-4

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

TANGER Ltd. Ostrava

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

23. 5. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—