On a critical geometry of a crack arrested at a bimaterial interface

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00385401" target="_blank" >RIV/68081723:_____/12:00385401 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

On a critical geometry of a crack arrested at a bimaterial interface

Popis výsledku v původním jazyce

Surface crack propagation in a thin soft protective layer on a massive stiffer substrate is analyzed using generalized linear elastic fracture mechanics. The growth of the initial crack is considered in both forward and sideways directions and the influence of the interface between the protective layer and massive substrate on the final crack configuration is investigated. It is shown that, depending on the elastic mismatch, the part of the crack front can be arrested at the interface protective layer/substrate and the rest of the crack grows continuously sideways only. The effective value of the stress intensity factor is used in order to predict the conditions under which the crack will propagate through the interface into the second material. Corresponding calculations have been made by finite element method.

Název v anglickém jazyce

On a critical geometry of a crack arrested at a bimaterial interface

Popis výsledku anglicky

Surface crack propagation in a thin soft protective layer on a massive stiffer substrate is analyzed using generalized linear elastic fracture mechanics. The growth of the initial crack is considered in both forward and sideways directions and the influence of the interface between the protective layer and massive substrate on the final crack configuration is investigated. It is shown that, depending on the elastic mismatch, the part of the crack front can be arrested at the interface protective layer/substrate and the rest of the crack grows continuously sideways only. The effective value of the stress intensity factor is used in order to predict the conditions under which the crack will propagate through the interface into the second material. Corresponding calculations have been made by finite element method.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

14th International conference Applied Mechanics 2012 - Conference proceedings

ISBN

978-80-261-0097-3

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

141-144

Název nakladatele

Západočeská univerzita v Plzni

Místo vydání

Plzeň

Místo konání akce

Plzeň

Datum konání akce

16. 4. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—