Embrittlement of ferritic 14%Cr ODS steel in air and in Pb/Pb-Bi coolants at elevated temperatures
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00385472" target="_blank" >RIV/68081723:_____/12:00385472 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Embrittlement of ferritic 14%Cr ODS steel in air and in Pb/Pb-Bi coolants at elevated temperatures
Popis výsledku v původním jazyce
The work was focused to describing influence of long-time high-temperature exposition of the ferritic 14%Cr ODS steel to the liquid Pb and Pb-Bi metals environments. The steel was during exposition in the liquid Pb and Pb-Bi at 600°C and 550°C respectively depleted from Cr and Ti formed with Pb and Bi the surface oxide scale. In addition the isothermal ageing of the steel at 650°C caused precipitates coarsening and porosity development by dislocation annealing in the bulk of the steel. Tensile and impact bend tests reveals outstanding embrittlement of the isothermally aged ODS steel and the steel after exposition to the liquid Pb and Pb-Bi compared with the steel in as-received state.
Název v anglickém jazyce
Embrittlement of ferritic 14%Cr ODS steel in air and in Pb/Pb-Bi coolants at elevated temperatures
Popis výsledku anglicky
The work was focused to describing influence of long-time high-temperature exposition of the ferritic 14%Cr ODS steel to the liquid Pb and Pb-Bi metals environments. The steel was during exposition in the liquid Pb and Pb-Bi at 600°C and 550°C respectively depleted from Cr and Ti formed with Pb and Bi the surface oxide scale. In addition the isothermal ageing of the steel at 650°C caused precipitates coarsening and porosity development by dislocation annealing in the bulk of the steel. Tensile and impact bend tests reveals outstanding embrittlement of the isothermally aged ODS steel and the steel after exposition to the liquid Pb and Pb-Bi compared with the steel in as-received state.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP108%2F10%2F0466" target="_blank" >GAP108/10/0466: Predikce lomového chování konstrukčních ocelí na základě kvantifikace lokální odezvy materiálu</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
New Methods of Damage and Failure Analysis of Structural Parts
ISBN
978-80-248-2802-2
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
437-442
Název nakladatele
VŠB-TU Ostrava
Místo vydání
Ostrava
Místo konání akce
Ostrava
Datum konání akce
10. 9. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—