High Temperature Fatigue Behaviour of Third Generation of TiAl Alloys

Popis výsledku v původním jazyce

Low cycle fatigue properties of lamellar TiAl with 7.8 at.% Nb were studied at four temperatures: room temperature, 700, 750 and 800 °C. Up to 750 °C, stable cyclic behaviour is observed while cyclic softening is characteristic for 800°C. The strength ofthe alloy is still high even at 800 °C. The TEM observation did not reveal any substantial changes in the microstructure due to the cycling at RT. At 750 °C, the lamellar structure was in some places destroyed by cyclic plasticity and pure g-phase islands with high density of dislocation debris were formed. At 800 °C, the domains without lamellar structure cover about 10% of inspected volume and are almost dislocation free. The results show that the diffusion processes leading to vanishing of small prizmatic dislocation loops start to operate between 750 and 800 °C. The destruction of lamellar microstructure and annealing of dislocation debris is the reason for cyclic softening at 800 °C.

Název v anglickém jazyce

High Temperature Fatigue Behaviour of Third Generation of TiAl Alloys

Popis výsledku anglicky

Low cycle fatigue properties of lamellar TiAl with 7.8 at.% Nb were studied at four temperatures: room temperature, 700, 750 and 800 °C. Up to 750 °C, stable cyclic behaviour is observed while cyclic softening is characteristic for 800°C. The strength ofthe alloy is still high even at 800 °C. The TEM observation did not reveal any substantial changes in the microstructure due to the cycling at RT. At 750 °C, the lamellar structure was in some places destroyed by cyclic plasticity and pure g-phase islands with high density of dislocation debris were formed. At 800 °C, the domains without lamellar structure cover about 10% of inspected volume and are almost dislocation free. The results show that the diffusion processes leading to vanishing of small prizmatic dislocation loops start to operate between 750 and 800 °C. The destruction of lamellar microstructure and annealing of dislocation debris is the reason for cyclic softening at 800 °C.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the 16th International Colloquium Mechanical Fatigue of Materials

ISBN

978-80-87434-05-5

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

143-148

Název nakladatele

Ústav fyziky materiálů AV ČR, v. v. i.

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

24. 9. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—