Dislocation densities and internal stress in Ni3Al
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00386754" target="_blank" >RIV/68081723:_____/13:00386754 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1080/14786435.2012.706371" target="_blank" >http://dx.doi.org/10.1080/14786435.2012.706371</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1080/14786435.2012.706371" target="_blank" >10.1080/14786435.2012.706371</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Dislocation densities and internal stress in Ni3Al
Popis výsledku v původním jazyce
Dislocation densities have been measured in Ni3Al(Hf) single crystals after deformation at various temperatures and strains. In addition, effective and athermal stresses have been determined by strain dip tests. A model is proposed for the strength anomaly domain which correlates the athermal part of the stress with the operation of dislocation sources, to compensate for the strong dislocation exhaustion. Dislocation density data, which evidence an anomaly in the density with temperature over the stressanomaly domain, are shown to support this model predictions between 373K and 683K for plastic strains larger than 3. 10 -2 but not at yield. In addition, the presence of Hf atoms (3.3 at. %) induces a friction stress close to 63 MPa.
Název v anglickém jazyce
Dislocation densities and internal stress in Ni3Al
Popis výsledku anglicky
Dislocation densities have been measured in Ni3Al(Hf) single crystals after deformation at various temperatures and strains. In addition, effective and athermal stresses have been determined by strain dip tests. A model is proposed for the strength anomaly domain which correlates the athermal part of the stress with the operation of dislocation sources, to compensate for the strong dislocation exhaustion. Dislocation density data, which evidence an anomaly in the density with temperature over the stressanomaly domain, are shown to support this model predictions between 373K and 683K for plastic strains larger than 3. 10 -2 but not at yield. In addition, the presence of Hf atoms (3.3 at. %) induces a friction stress close to 63 MPa.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Philosophical Magazine
ISSN
1478-6435
e-ISSN
—
Svazek periodika
93
Číslo periodika v rámci svazku
1-3
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
10
Strana od-do
50-59
Kód UT WoS článku
000315719700005
EID výsledku v databázi Scopus
—