Understandiong of low cycle fatigue behaviour of ODS steels
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00398749" target="_blank" >RIV/68081723:_____/13:00398749 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Understandiong of low cycle fatigue behaviour of ODS steels
Popis výsledku v původním jazyce
The low cycle fatigue life in the ODS Eurofer steel and in two 14Cr ODS ferritic steels produced in the CEA was analysed. The Coffin-Manson curve was measured. Substantial differences in fatigue life were found. Surface relief observation after failure revealed places of crack initiation and its influence on fatigue life was explained. Small fatigue crack growth rate measurement was carried out in the ODS Eurofer steel and in one of the 14Cr ODS ferritic steels. It was determined that fatigue crack growin the 14Cr ODS ferritic steel is significantly faster than in the ODS Eurofer steel. All measured data are discussed and differences between particular steels are explained in relation to the Coffin-Manson plot.
Název v anglickém jazyce
Understandiong of low cycle fatigue behaviour of ODS steels
Popis výsledku anglicky
The low cycle fatigue life in the ODS Eurofer steel and in two 14Cr ODS ferritic steels produced in the CEA was analysed. The Coffin-Manson curve was measured. Substantial differences in fatigue life were found. Surface relief observation after failure revealed places of crack initiation and its influence on fatigue life was explained. Small fatigue crack growth rate measurement was carried out in the ODS Eurofer steel and in one of the 14Cr ODS ferritic steels. It was determined that fatigue crack growin the 14Cr ODS ferritic steel is significantly faster than in the ODS Eurofer steel. All measured data are discussed and differences between particular steels are explained in relation to the Coffin-Manson plot.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the Seventh International Conference on Low Cycle Fatigue - LCF7
ISBN
978-3-9814516-2-7
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
439-444
Název nakladatele
DMV
Místo vydání
Berlín
Místo konání akce
Aachen
Datum konání akce
9. 9. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—