Fatigue life of cast Inconel 713LC with/without protective diffusion coating under bending, torsion and their combination

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00421927" target="_blank" >RIV/68081723:_____/13:00421927 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26620/13:PU104011

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.engfracmech.2013.01.001" target="_blank" >http://dx.doi.org/10.1016/j.engfracmech.2013.01.001</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.engfracmech.2013.01.001" target="_blank" >10.1016/j.engfracmech.2013.01.001</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue life of cast Inconel 713LC with/without protective diffusion coating under bending, torsion and their combination

Popis výsledku v původním jazyce

Fatigue behaviour of cylindrical specimens made of cast Inconel 713LC nickel-based superalloy with/without diffusion aluminide and Cr-modified aluminide protective coatings was studied under bending, torsion and combined bending?torsion loading regimes.Experiments were conducted at room temperature by using sinusoidal loading of a frequency f 30 Hz. It was found that the presence of either coating system enhances the high cycle fatigue strength for all tested loading regimes. In the low cycle fatigue region, the fatigue strength was slightly improved for torsional loading, while it was almost the same or modestly lower for loading regimes with non-zero bending component. This behaviour seems to be linked to different nucleation efficiency of secondary-phase particles within the diffusion zone.

Název v anglickém jazyce

Fatigue life of cast Inconel 713LC with/without protective diffusion coating under bending, torsion and their combination

Popis výsledku anglicky

Fatigue behaviour of cylindrical specimens made of cast Inconel 713LC nickel-based superalloy with/without diffusion aluminide and Cr-modified aluminide protective coatings was studied under bending, torsion and combined bending?torsion loading regimes.Experiments were conducted at room temperature by using sinusoidal loading of a frequency f 30 Hz. It was found that the presence of either coating system enhances the high cycle fatigue strength for all tested loading regimes. In the low cycle fatigue region, the fatigue strength was slightly improved for torsional loading, while it was almost the same or modestly lower for loading regimes with non-zero bending component. This behaviour seems to be linked to different nucleation efficiency of secondary-phase particles within the diffusion zone.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

—

Svazek periodika

110

Číslo periodika v rámci svazku

SEP

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

459-467

Kód UT WoS článku

000328176100034

EID výsledku v databázi Scopus

—