Microstructure and Local Mechanical Properties of Cu-Co Alloys after Severe Plastic Deformation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00396339" target="_blank" >RIV/68081723:_____/14:00396339 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216224:14310/14:00095733

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.586.100" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.586.100</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.586.100" target="_blank" >10.4028/www.scientific.net/KEM.586.100</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructure and Local Mechanical Properties of Cu-Co Alloys after Severe Plastic Deformation

Popis výsledku v původním jazyce

Microstructure of Cu-2wt.%Co alloy after various heat treatment (and hence with various phase constitution) was studied after equal-channel angular pressing (ECAP) using transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) technique in a scanning electron microscope (SEM). We also focused on local mechanical properties measured across the section perpendicular to the ECAP extrusion direction. Starting from the grain size well above 1mm in the Cu-2wt.%Co solid solution, ECAPsubsequently reduces grain size down to the submicron level. A comparison with pure Cu shows that the grain size homogenization is shifted towards higher number of ECAP passes. Fine dispersion of precipitates further slows down the grain refinement andgrain size homogenization during ECAP processing. Local mechanical properties measured across the section perpendicular to the ECAP extrusion direction reveal systematic inhomogeneities of deformed microstructure caused by local gradients

Název v anglickém jazyce

Microstructure and Local Mechanical Properties of Cu-Co Alloys after Severe Plastic Deformation

Popis výsledku anglicky

Microstructure of Cu-2wt.%Co alloy after various heat treatment (and hence with various phase constitution) was studied after equal-channel angular pressing (ECAP) using transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) technique in a scanning electron microscope (SEM). We also focused on local mechanical properties measured across the section perpendicular to the ECAP extrusion direction. Starting from the grain size well above 1mm in the Cu-2wt.%Co solid solution, ECAPsubsequently reduces grain size down to the submicron level. A comparison with pure Cu shows that the grain size homogenization is shifted towards higher number of ECAP passes. Fine dispersion of precipitates further slows down the grain refinement andgrain size homogenization during ECAP processing. Local mechanical properties measured across the section perpendicular to the ECAP extrusion direction reveal systematic inhomogeneities of deformed microstructure caused by local gradients

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F11%2F2260" target="_blank" >GAP108/11/2260: Vztah mezi mikrostrukturou a creepovým chováním precipitačně zpevněných slitin připravených metodou ECAP</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Local Mechanical Properties IX

ISBN

978-3-03785-876-9

ISSN

1013-9826

e-ISSN

—

Počet stran výsledku

4

Strana od-do

100-103

Název nakladatele

Trans Tech Publications

Místo vydání

Zurich

Místo konání akce

Levoča

Datum konání akce

7. 11. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000336633500024