CARBON DIFFUSION IN CARBON-SUPERSATURATED 9CR-1MO STEEL: ANOMALOUS TEMPERATURE DEPENDENCE OF CARBON DIFFUSIVITY

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00432049" target="_blank" >RIV/68081723:_____/14:00432049 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

CARBON DIFFUSION IN CARBON-SUPERSATURATED 9CR-1MO STEEL: ANOMALOUS TEMPERATURE DEPENDENCE OF CARBON DIFFUSIVITY

Popis výsledku v původním jazyce

Carbon diffusion was studied in temperature interval 573 - 1073 K in carbon-supersaturated surface layer of 9Cr?1Mo steel P91 and in model Fe-15Cr binary alloy. Extremely low carbon diffusion coefficient D (by 3 orders of magnitude lower than the value Deq in material with equilibrium carbon concentration) was observed in carburized surface region of Fe-15Cr. Similar results were obtained for P91 above the temperature T n 800 K. However, below T n , the values of D measured in P91 increased and approached the value of D eq . It seems that the non-Arrhenius behaviour of P91 steel around T n may be ascribed to the ? ? + ?? phase decomposition. Possible effect of nitrogen upon the low-temperature increase in D in P91 steel was excluded.

Název v anglickém jazyce

CARBON DIFFUSION IN CARBON-SUPERSATURATED 9CR-1MO STEEL: ANOMALOUS TEMPERATURE DEPENDENCE OF CARBON DIFFUSIVITY

Popis výsledku anglicky

Carbon diffusion was studied in temperature interval 573 - 1073 K in carbon-supersaturated surface layer of 9Cr?1Mo steel P91 and in model Fe-15Cr binary alloy. Extremely low carbon diffusion coefficient D (by 3 orders of magnitude lower than the value Deq in material with equilibrium carbon concentration) was observed in carburized surface region of Fe-15Cr. Similar results were obtained for P91 above the temperature T n 800 K. However, below T n , the values of D measured in P91 increased and approached the value of D eq . It seems that the non-Arrhenius behaviour of P91 steel around T n may be ascribed to the ? ? + ?? phase decomposition. Possible effect of nitrogen upon the low-temperature increase in D in P91 steel was excluded.

Druh

D - Stať ve sborníku

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2014: 23rd International Conference on Metallurgy and Materials

ISBN

978-80-87294-52-9

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

Tanger Ltd

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

21. 5. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—