Small Punch Tests at Oxide Scales Surface of Structural Steel and Low Silicon Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00434807" target="_blank" >RIV/68081723:_____/14:00434807 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/14:PU110545

Výsledek na webu

<a href="http://dx.doi.org/10.1007/s11085-014-9492-5" target="_blank" >http://dx.doi.org/10.1007/s11085-014-9492-5</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s11085-014-9492-5" target="_blank" >10.1007/s11085-014-9492-5</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Small Punch Tests at Oxide Scales Surface of Structural Steel and Low Silicon Steel

Popis výsledku v původním jazyce

This work is focused on the study of the behavior of oxide scale layers grown on two types of steel: plain carbon steel and silicon-alloyed steel. The small punch test method was chosen to study the mechanical properties of oxide scale layers. Several specimens were prepared from both materials and exposed to 1,000 C for different oxidation times to obtain the desired scale layers. When the oxidation process was complete, oxide layers of varying thickness, composed mainly of hematite and magnetite, werecreated. The specimens were used for testing at temperatures between 600 and 900 C.

Název v anglickém jazyce

Small Punch Tests at Oxide Scales Surface of Structural Steel and Low Silicon Steel

Popis výsledku anglicky

This work is focused on the study of the behavior of oxide scale layers grown on two types of steel: plain carbon steel and silicon-alloyed steel. The small punch test method was chosen to study the mechanical properties of oxide scale layers. Several specimens were prepared from both materials and exposed to 1,000 C for different oxidation times to obtain the desired scale layers. When the oxidation process was complete, oxide layers of varying thickness, composed mainly of hematite and magnetite, werecreated. The specimens were used for testing at temperatures between 600 and 900 C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.20.0188" target="_blank" >EE2.3.20.0188: Multidisciplinární tým pro výzkum a aplikace tepelných procesů</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Oxidation of Metals

ISSN

0030-770X

e-ISSN

—

Svazek periodika

82

Číslo periodika v rámci svazku

3-4

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

14

Strana od-do

297-310

Kód UT WoS článku

000341923900009

EID výsledku v databázi Scopus

—