Modified compact tension test: The influence of the steel bars position

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00434836" target="_blank" >RIV/68081723:_____/14:00434836 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26110/14:PU113789

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Modified compact tension test: The influence of the steel bars position

Popis výsledku v původním jazyce

Testing and analysis of fatigue behavior of homogeneous materials, such as concrete or other cement based composites, are one major problem being studied in this scientific field. In this contribution, adaptation of the compact tension test, well known its use in the testing of metallic materials, is pursued for crack propagation rate measurement on cement based composites using cylindrical specimens. In particular, the influence of the steel bars position on the fracture parameters is studied in the modified compact tension test. The numerical study is performed by ATENA 2D. The results are compared by Load-COD diagrams and the variation of the fracture parameters values is discussed.

Název v anglickém jazyce

Modified compact tension test: The influence of the steel bars position

Popis výsledku anglicky

Testing and analysis of fatigue behavior of homogeneous materials, such as concrete or other cement based composites, are one major problem being studied in this scientific field. In this contribution, adaptation of the compact tension test, well known its use in the testing of metallic materials, is pursued for crack propagation rate measurement on cement based composites using cylindrical specimens. In particular, the influence of the steel bars position on the fracture parameters is studied in the modified compact tension test. The numerical study is performed by ATENA 2D. The results are compared by Load-COD diagrams and the variation of the fracture parameters values is discussed.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.20.0214" target="_blank" >EE2.3.20.0214: Rozvoj lidských zdrojů ve výzkumu fyzikálních a materiálových vlastností modelových, nově vyvíjených a inženýrsky aplikovaných materiálů</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Engineering mechanics 2014

ISBN

978-80-214-4871-1

ISSN

1805-8248

e-ISSN

—

Počet stran výsledku

4

Strana od-do

220-223

Název nakladatele

Brno University of Technology

Místo vydání

Brno

Místo konání akce

Svratka

Datum konání akce

12. 5. 2014

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—