Mechanical alloying of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic material of Permalloy type
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00435587" target="_blank" >RIV/68081723:_____/14:00435587 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical alloying of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic material of Permalloy type
Popis výsledku v původním jazyce
The paper describes preparation of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic alloy of Permalloy type by mechanical alloying from atomic powders. The powders were mechanically alloyed by high-energy ball milling in planetary mill under an air atmosphere. Comparing results from electron energy chemical analysis and X-ray diffraction analysis it was found that hardness of alloy corresponds to the chemical and phase homogeneity of composite powder. After 24 hours of milling the one phase homogenous composite powder was prepared having Vickers hardness about 750 HV1 and coercivity about 40 A.m-1. Further alloying led to powder grain size and crystallinite size refinement. This process was accompanied with defects amount increasing and thus with increasingof coercivity up to 120 A.m-1 after alloying for 120 hours.
Název v anglickém jazyce
Mechanical alloying of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic material of Permalloy type
Popis výsledku anglicky
The paper describes preparation of 80Ni-14.7Fe-4.4Mo-0.5Mn-0.3Si soft magnetic alloy of Permalloy type by mechanical alloying from atomic powders. The powders were mechanically alloyed by high-energy ball milling in planetary mill under an air atmosphere. Comparing results from electron energy chemical analysis and X-ray diffraction analysis it was found that hardness of alloy corresponds to the chemical and phase homogeneity of composite powder. After 24 hours of milling the one phase homogenous composite powder was prepared having Vickers hardness about 750 HV1 and coercivity about 40 A.m-1. Further alloying led to powder grain size and crystallinite size refinement. This process was accompanied with defects amount increasing and thus with increasingof coercivity up to 120 A.m-1 after alloying for 120 hours.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA14-25246S" target="_blank" >GA14-25246S: Pokročilé ODS oceli pro aplikace v prostředí tavenin těžkých kovů</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Powder Metallurgy Progress
ISSN
1335-8987
e-ISSN
—
Svazek periodika
14
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
7
Strana od-do
208-214
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—