FRACTURE MECHANICS ASSESSMENT OF CRACKED WELDED POLYOLEFIN PIPES

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00465158" target="_blank" >RIV/68081723:_____/14:00465158 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

FRACTURE MECHANICS ASSESSMENT OF CRACKED WELDED POLYOLEFIN PIPES

Popis výsledku v původním jazyce

The aim of this paper is to present methodology for estimation of fracture mechanics parameters in polyolefin pipes with an axially oriented crack using three dimensional numerical analyses. Linear elastic fracture mechanics is used for description of fracture behavior. In the paper, three different variants of pipe weld with an internal axial semi-elliptical crack are studied. Numerical models correspond to a cracked pipe containing material nonhomogeneity in the welding area caused by welding process. A critical locations of the crack initiated along the pipe wall is found and the stress intensity factor for such cracks with real crack shape are numerically estimated in these critical locations. The methodology presented here can be used for estimation of residual lifetime of welded polymer pipes containing crack.

Název v anglickém jazyce

FRACTURE MECHANICS ASSESSMENT OF CRACKED WELDED POLYOLEFIN PIPES

Popis výsledku anglicky

The aim of this paper is to present methodology for estimation of fracture mechanics parameters in polyolefin pipes with an axially oriented crack using three dimensional numerical analyses. Linear elastic fracture mechanics is used for description of fracture behavior. In the paper, three different variants of pipe weld with an internal axial semi-elliptical crack are studied. Numerical models correspond to a cracked pipe containing material nonhomogeneity in the welding area caused by welding process. A critical locations of the crack initiated along the pipe wall is found and the stress intensity factor for such cracks with real crack shape are numerically estimated in these critical locations. The methodology presented here can be used for estimation of residual lifetime of welded polymer pipes containing crack.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Engineering Mechanics 2014. 20th International conference. May 12-15, 2014, Svratka, Czech Republic. Book of full texts

ISBN

978-80-214-4871-1

ISSN

1805-8248

e-ISSN

—

Počet stran výsledku

4

Strana od-do

396-399

Název nakladatele

Brno University of Technology. Institute of Solid Mechanics, Mechatronics and Biomechanics

Místo vydání

Brno

Místo konání akce

Svratka

Datum konání akce

12. 5. 2014

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000364573900092