Changes in microstructure and physical properties of skutterudites after severe plastic deformation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00440906" target="_blank" >RIV/68081723:_____/15:00440906 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1039/C4CP05230G" target="_blank" >http://dx.doi.org/10.1039/C4CP05230G</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1039/C4CP05230G" target="_blank" >10.1039/C4CP05230G</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Changes in microstructure and physical properties of skutterudites after severe plastic deformation
Popis výsledku v původním jazyce
The best p-type skutterudites with ZT gt 1.1 so far are didymium (DD) filled, Fe/Co substituted, Sb-based skutterudites. DD0.68Fe3CoSb12 was prepared using an annealing?reacting?melting?quenching technique followed by ball milling and hot pressing. Aftersevere plastic deformation via high-pressure torsion (HPT), no phase changes but particular structural variations were achieved, leading to modified transport properties with higher ZT values. Although after measurement-induced heating some of the HPT induced defects were annealed out, a still attractive ZT-value was preserved. In this paper we focus on explanations for these changes via TEM investigations, Raman spectroscopy and texture measurements.
Název v anglickém jazyce
Changes in microstructure and physical properties of skutterudites after severe plastic deformation
Popis výsledku anglicky
The best p-type skutterudites with ZT gt 1.1 so far are didymium (DD) filled, Fe/Co substituted, Sb-based skutterudites. DD0.68Fe3CoSb12 was prepared using an annealing?reacting?melting?quenching technique followed by ball milling and hot pressing. Aftersevere plastic deformation via high-pressure torsion (HPT), no phase changes but particular structural variations were achieved, leading to modified transport properties with higher ZT values. Although after measurement-induced heating some of the HPT induced defects were annealed out, a still attractive ZT-value was preserved. In this paper we focus on explanations for these changes via TEM investigations, Raman spectroscopy and texture measurements.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Physical Chemistry Chemical Physics
ISSN
1463-9076
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
3715-3722
Kód UT WoS článku
000348203200085
EID výsledku v databázi Scopus
2-s2.0-84921628487