High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00458479" target="_blank" >RIV/68081723:_____/16:00458479 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/16:PU117614

Výsledek na webu

<a href="http://dx.doi.org/10.1007/s12666-015-0817-0" target="_blank" >http://dx.doi.org/10.1007/s12666-015-0817-0</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s12666-015-0817-0" target="_blank" >10.1007/s12666-015-0817-0</a>

Jazyk výsledku

angličtina

Název v původním jazyce

High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures

Popis výsledku v původním jazyce

High cycle fatigue tests of the MAR-M 247 superalloy under constant load were conducted with the aim to determine S-N curves at temperatures 650, 800, 900 and 950 A degrees C. It has been found that the slope of the S-N curves reflects changes of the cyclic deformation mechanism with temperature. At temperatures 650 and partly at 800 A degrees C, fatigue crack propagation exhibits crystallographic character (propagation along the {111} system) in early stages of the fatigue life. The crystallographic mode of the fatigue crack propagation was found to disappear at temperatures 900 and 950 A degrees C.

Název v anglickém jazyce

High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures

Popis výsledku anglicky

High cycle fatigue tests of the MAR-M 247 superalloy under constant load were conducted with the aim to determine S-N curves at temperatures 650, 800, 900 and 950 A degrees C. It has been found that the slope of the S-N curves reflects changes of the cyclic deformation mechanism with temperature. At temperatures 650 and partly at 800 A degrees C, fatigue crack propagation exhibits crystallographic character (propagation along the {111} system) in early stages of the fatigue life. The crystallographic mode of the fatigue crack propagation was found to disappear at temperatures 900 and 950 A degrees C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Indian Institute of Metals. Transactions

ISSN

0972-2815

e-ISSN

—

Svazek periodika

69

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

IN - Indická republika

Počet stran výsledku

5

Strana od-do

393-397

Kód UT WoS článku

000368032700036

EID výsledku v databázi Scopus

2-s2.0-84954361027