The role of residual stresses in particulate composite with glass matrix
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00458483" target="_blank" >RIV/68081723:_____/16:00458483 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.665.173" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.665.173</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.665.173" target="_blank" >10.4028/www.scientific.net/KEM.665.173</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The role of residual stresses in particulate composite with glass matrix
Popis výsledku v původním jazyce
The particulate composites with glass matrix are widely used in many engineering applications. The mismatch of coefficients of thermal expansion during the fabrication process usually causes the presence of the residual stresses around particles. The influence and the understanding of the effects of residual stresses on the material response is required. The main aim of the present paper was to create a two-dimensional finite element model to analyze the influence of residual stresses on micro-crack behavior of glass and ceramics-based particulate composites. The maximum tangential stress criterion (MTS) was used to predict the direction of the micro-crack propagation. The modelled material was a kind of Low Temperature Co-fired Ceramics (LTCC) containing alumina particles embedded in a glass matrix. The influence of the micro-crack length and magnitude of loading on the micro-crack propagation path were investigated. The finite element software ANSYS was used. Conclusions of this paper can contribute to a better understanding of the propagation of micro-cracks in particulate composites in the field of residual stresses.
Název v anglickém jazyce
The role of residual stresses in particulate composite with glass matrix
Popis výsledku anglicky
The particulate composites with glass matrix are widely used in many engineering applications. The mismatch of coefficients of thermal expansion during the fabrication process usually causes the presence of the residual stresses around particles. The influence and the understanding of the effects of residual stresses on the material response is required. The main aim of the present paper was to create a two-dimensional finite element model to analyze the influence of residual stresses on micro-crack behavior of glass and ceramics-based particulate composites. The maximum tangential stress criterion (MTS) was used to predict the direction of the micro-crack propagation. The modelled material was a kind of Low Temperature Co-fired Ceramics (LTCC) containing alumina particles embedded in a glass matrix. The influence of the micro-crack length and magnitude of loading on the micro-crack propagation path were investigated. The finite element software ANSYS was used. Conclusions of this paper can contribute to a better understanding of the propagation of micro-cracks in particulate composites in the field of residual stresses.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advances in Fracture and Damage Mechanics XIV
ISBN
978-3-03835-541-0
ISSN
1013-9826
e-ISSN
—
Počet stran výsledku
4
Strana od-do
173-176
Název nakladatele
Trans Tech Publications
Místo vydání
Zurich
Místo konání akce
Budva
Datum konání akce
21. 9. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—