Thermally Induced Structural Transformations of Fe40Ni40P14B6 Amorphous Alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00463858" target="_blank" >RIV/68081723:_____/16:00463858 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s11661-015-3226-4" target="_blank" >http://dx.doi.org/10.1007/s11661-015-3226-4</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11661-015-3226-4" target="_blank" >10.1007/s11661-015-3226-4</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Thermally Induced Structural Transformations of Fe40Ni40P14B6 Amorphous Alloy
Popis výsledku v původním jazyce
Thermal stability and thermally induced structural transformations of Fe40Ni40P14B6 amorphous alloy were examined under non-isothermal and isothermal conditions. Formation of metastable alpha-(Fe,Ni), and stable gamma-(Fe,Ni) and (Fe,Ni)(3)(P,B) crystalline phases as the main crystallization products was observed, while the presence of small amounts of other crystalline phases like Fe23B6 and Fe2NiB was indicated by electron diffraction in HRTEM. Thermomagnetic curve indicated that Fe content in different crystalline phases is very different, resulting in markedly different Curie temperatures after crystallization. Transmission electron microscopy and atomic force microscopy study suggested multiple-layered platelet-shaped morphology, both on the surface and in the bulk of the crystallized alloy sample. The thermal treatment heating rate and maximum temperature affected surface roughness and grain size inhomogeneity.
Název v anglickém jazyce
Thermally Induced Structural Transformations of Fe40Ni40P14B6 Amorphous Alloy
Popis výsledku anglicky
Thermal stability and thermally induced structural transformations of Fe40Ni40P14B6 amorphous alloy were examined under non-isothermal and isothermal conditions. Formation of metastable alpha-(Fe,Ni), and stable gamma-(Fe,Ni) and (Fe,Ni)(3)(P,B) crystalline phases as the main crystallization products was observed, while the presence of small amounts of other crystalline phases like Fe23B6 and Fe2NiB was indicated by electron diffraction in HRTEM. Thermomagnetic curve indicated that Fe content in different crystalline phases is very different, resulting in markedly different Curie temperatures after crystallization. Transmission electron microscopy and atomic force microscopy study suggested multiple-layered platelet-shaped morphology, both on the surface and in the bulk of the crystallized alloy sample. The thermal treatment heating rate and maximum temperature affected surface roughness and grain size inhomogeneity.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/1M0512" target="_blank" >1M0512: Centrrum výzkumu práškových nanomateriálů</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Metallurgical and Materials Transactions A
ISSN
1073-5623
e-ISSN
—
Svazek periodika
47A
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
8
Strana od-do
260-267
Kód UT WoS článku
000367468100027
EID výsledku v databázi Scopus
2-s2.0-84946866902