Distinguishing between slip and twinning events during nanoindentation of magnesium alloy AZ31

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00465734" target="_blank" >RIV/68081723:_____/16:00465734 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.scriptamat.2015.07.034" target="_blank" >http://dx.doi.org/10.1016/j.scriptamat.2015.07.034</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2015.07.034" target="_blank" >10.1016/j.scriptamat.2015.07.034</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Distinguishing between slip and twinning events during nanoindentation of magnesium alloy AZ31

Popis výsledku v původním jazyce

Nanoindentation was performed in selected grain orientations close to [11-20] and [10-10] in magnesium alloy Mg–3Al–1Zn. The atomic force microscopy (AFM) and electron backscatter diffraction (EBSD) were used to examine the nanoindentation imprint. Two critical events, yielding and pop-in were observed in the depth–load curves. Slip trace analysis suggests that basal slip is responsible for yielding. The following pop-in events at higher loads are associated with the appearance {10-12} twins on the surface. The critical resolved shear stress (CRSS) was estimated to be in the range of 220–400 MPa for the initiation of basal slip.

Název v anglickém jazyce

Distinguishing between slip and twinning events during nanoindentation of magnesium alloy AZ31

Popis výsledku anglicky

Nanoindentation was performed in selected grain orientations close to [11-20] and [10-10] in magnesium alloy Mg–3Al–1Zn. The atomic force microscopy (AFM) and electron backscatter diffraction (EBSD) were used to examine the nanoindentation imprint. Two critical events, yielding and pop-in were observed in the depth–load curves. Slip trace analysis suggests that basal slip is responsible for yielding. The following pop-in events at higher loads are associated with the appearance {10-12} twins on the surface. The critical resolved shear stress (CRSS) was estimated to be in the range of 220–400 MPa for the initiation of basal slip.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.20.0197" target="_blank" >EE2.3.20.0197: Víceoborový výzkumný tým v oblasti designu materiálů a jeho zapojení do mezinárodní kooperace</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

110

Číslo periodika v rámci svazku

JAN

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

4

Strana od-do

10-13

Kód UT WoS článku

000362923500004

EID výsledku v databázi Scopus

2-s2.0-84943358301