HYDROGENATION OF CHOSEN MgMXN INTERMETALLICS (X=Al, Ga, In, Si, Sn)

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00473834" target="_blank" >RIV/68081723:_____/16:00473834 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

HYDROGENATION OF CHOSEN MgMXN INTERMETALLICS (X=Al, Ga, In, Si, Sn)

Popis výsledku v původním jazyce

Hydrogen sorption in chosen intermetallics MgmXn (Mg17Al12 , Mg2Ga, mixture of beta-Mg-In phases, Mg2Si and Mg2Sn) formed by magnesium and elements from the 13 th (X: Al, Ga, In) and 14 th (X: Si, Sn) groups was studied between the room temperature and T = 350 °C. Hydrogen pressure p varied from 10-3 MPa to 6 MPa.nHydrogen solubility in alpha phase (solid solution of hydrogen in MgmXn before the hydride phase was nucleated) was close to hydrogen solubility in pure Mg. Concentration cH of hydrogen solved in Mg m X n depended linearly on pressure p , dependence of cH on temperature T was relatively weak. MgH2 was the main hydrogen storage phase in all the compounds MgmXn . Nucleation of MgH2 at 350 °C was observed at pressure above approximately 1 MPa in Mg17Al12 and above 2 Ma in other compounds. Maximum values of c H in hydride-containing compounds MgmXn detected at T = 350 °C depended on the stability of MgmXn .

Název v anglickém jazyce

HYDROGENATION OF CHOSEN MgMXN INTERMETALLICS (X=Al, Ga, In, Si, Sn)

Popis výsledku anglicky

Hydrogen sorption in chosen intermetallics MgmXn (Mg17Al12 , Mg2Ga, mixture of beta-Mg-In phases, Mg2Si and Mg2Sn) formed by magnesium and elements from the 13 th (X: Al, Ga, In) and 14 th (X: Si, Sn) groups was studied between the room temperature and T = 350 °C. Hydrogen pressure p varied from 10-3 MPa to 6 MPa.nHydrogen solubility in alpha phase (solid solution of hydrogen in MgmXn before the hydride phase was nucleated) was close to hydrogen solubility in pure Mg. Concentration cH of hydrogen solved in Mg m X n depended linearly on pressure p , dependence of cH on temperature T was relatively weak. MgH2 was the main hydrogen storage phase in all the compounds MgmXn . Nucleation of MgH2 at 350 °C was observed at pressure above approximately 1 MPa in Mg17Al12 and above 2 Ma in other compounds. Maximum values of c H in hydride-containing compounds MgmXn detected at T = 350 °C depended on the stability of MgmXn .

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20303 - Thermodynamics

Projekt

<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANOCON 2016. 8th International Conference on Nanomaterials - Research and Application

ISBN

978-80-87294-68-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

715-720

Název nakladatele

TANGER

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

19. 10. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000410656100124