Study of Influence of Residual Stresses on Crack Propagation in Particulate Ceramic Composites

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00469173" target="_blank" >RIV/68081723:_____/17:00469173 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/17:PU125251

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258.178" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.258.178</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258.178" target="_blank" >10.4028/www.scientific.net/SSP.258.178</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Study of Influence of Residual Stresses on Crack Propagation in Particulate Ceramic Composites

Popis výsledku v původním jazyce

The aim of the present work is to analzye the influence of residual stresses in the particulate ceramic composite on the crack propagation. The crack propagation direction was estimated by using Sih´s criterion based on the strain energy density factor. A two-dimensional finite element model was developed for determination of crack path. The residual stresses resulting from the mismatch of coefficients of thermal expansion during the facrication process of the composite were implemented to the computational model. The effect of the particles shape on the crack peopagation was investigated. Conclusions of this paper can contribute to a better understanding of the propagation of micro-cracks in particulate composites in the field of residual stresses.

Název v anglickém jazyce

Study of Influence of Residual Stresses on Crack Propagation in Particulate Ceramic Composites

Popis výsledku anglicky

The aim of the present work is to analzye the influence of residual stresses in the particulate ceramic composite on the crack propagation. The crack propagation direction was estimated by using Sih´s criterion based on the strain energy density factor. A two-dimensional finite element model was developed for determination of crack path. The residual stresses resulting from the mismatch of coefficients of thermal expansion during the facrication process of the composite were implemented to the computational model. The effect of the particles shape on the crack peopagation was investigated. Conclusions of this paper can contribute to a better understanding of the propagation of micro-cracks in particulate composites in the field of residual stresses.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

<a href="/cs/project/GA15-09347S" target="_blank" >GA15-09347S: Role reziduálních napětí v životnosti keramických kompozitů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure & Micromechanics of Fracture VIII

ISBN

978-3-03835-626-4

ISSN

1662-9779

e-ISSN

—

Počet stran výsledku

4

Strana od-do

"Č. 258 (2017)"

Název nakladatele

Trans Tech Publications

Místo vydání

Zürrich

Místo konání akce

Brno

Datum konání akce

27. 6. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—