Small Punch Testing of Sanicro 25 Steel and its Correlation with Uniaxial Tests
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00479772" target="_blank" >RIV/68081723:_____/17:00479772 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.734.70" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.734.70</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.734.70" target="_blank" >10.4028/www.scientific.net/KEM.734.70</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Small Punch Testing of Sanicro 25 Steel and its Correlation with Uniaxial Tests
Popis výsledku v původním jazyce
Small punch testing under constant deflection rate, constant force and constant deflectionn(i.e. force relaxation) were performed on the new austenitic steel Sanicro 25. Constant deflectionnrate experiments were correlated to uniaxial tensile tests at room temperature and 700°C with thenhelp of several empirical relationships. Small punch creep testing was performed in as receivednstate. Correlation of the small punch results with uniaxial creep test results was done and thenforce/stress ratio psi and kSP parameter were determined. The constant deflection small punch testnwas correlated with the uniaxial stress relaxation test and good agreement was reached.
Název v anglickém jazyce
Small Punch Testing of Sanicro 25 Steel and its Correlation with Uniaxial Tests
Popis výsledku anglicky
Small punch testing under constant deflection rate, constant force and constant deflectionn(i.e. force relaxation) were performed on the new austenitic steel Sanicro 25. Constant deflectionnrate experiments were correlated to uniaxial tensile tests at room temperature and 700°C with thenhelp of several empirical relationships. Small punch creep testing was performed in as receivednstate. Correlation of the small punch results with uniaxial creep test results was done and thenforce/stress ratio psi and kSP parameter were determined. The constant deflection small punch testnwas correlated with the uniaxial stress relaxation test and good agreement was reached.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Small Sample Test Technique
ISBN
978-3-0357-1106-6
ISSN
1013-9826
e-ISSN
—
Počet stran výsledku
7
Strana od-do
70-76
Název nakladatele
Trans Tech Publications
Místo vydání
Zürich
Místo konání akce
Shanghai
Datum konání akce
12. 10. 2016
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—